| Doublemer |
Chemical Description |
Characteristics |
Applications |
| 120 |
2-Hydroxy-3-phenoxypropyl acrylate |
• Good flexibility
• Good adhesion
• Low shrinkage |
• Coatings for paper & plastics
• UV inks
• UV adhesives |
| 127-TP20 |
Bisphenol A epoxy diacrylate |
• Light color
• Very high gloss
• Fast curing speed
• Good heat and chemical resistance
• High surface hardness |
• Clear coatings for paper, paper board, wood, chipboard
and rigid plastics
• Overprint varnishes
• Lithographic and screen ink
• Wood sealers
• Paper upgrading
• Laminating adhesives
• Fast cure coatings |
| 186 |
Epoxidised soya bean oil acrylate |
• Enhanced adhesion over paper and metal
• Good surface appearance
• Good pigment wetting
• Improved substrate wetting |
• Overprinting varnishes
• Coatings for paper & plastics
• Wood top coat with smooth surface
• Ink binder with good wetting property
• Adhesives |
| 1636 |
Novolac epoxy acrylate diluted in 40% TMPTA |
• Excellent heat resistance
• Fast cure rate
• Excellent chemical resistance
• Good hardness |
• Clear coatings on metal
• Wood top coatings
• Solder mask inks
• Heat, chemical resist coatings
• Adhesion binders for metal |
| 1656 |
Cresol Novolac epoxy acrylate |
• Excellent abrasion and scratching resistance
• Good thermal resistance properties
• Excellent chemical resistance
• Good adhesion on metal |
• Coatings on metal
• PCB marking ink
• Heat resist coatings
• Solder resisit |
| 1701 |
Modified Bisphenol A epoxy diacrylate |
• Higher flexibility than standard bisphenol A epoxy
acrylate
• Excellent chemical resistance
• Very high gloss
• Good abrasion resistance |
• Adhesive for paper and film lamination
• Coatings for paper, Wood and plastics
• Lithographic and screen inks vehicles |
| 1702 |
Bisphenol A epoxy diacrylate (modified by fatty acid) |
• Flexibility superior to standard bisphenol A epoxy
acrylates
• High gloss
• Excellent water and chemical resistance
• Good flow and leveling |
• Vehicles for metal decorating inks and clear coatings
• Overprint varnishes
• Coatings for paper and plastics
• Lithographic and screen ink vehicles |
| 1703 |
Bisphenol A epoxy diacrylate (modified
by amine) |
• Good UV/EB cure reactivity
• High gloss
• Good flexibility and adhesion
• Good surface hardness
• Good solvent resistance
• Excellent chemical resistance |
• Vehicles for metal decorating inks and clear coatings
• Top coats for wood
• Coatings for paper and plastics
• Lithographic and screen ink vehicles |
| Doublemer |
Typical
Physical & Chemical Properties |
| Functionality |
Appearance |
Color
(Gardner) |
Acid
Value
(mg KOH/g) |
Viscosity
(cps at 25°C) |
| 120 |
1 |
Clear & clean |
1 |
1 |
150～200 |
| 127-TP20 |
2 |
Clear & clean |
1 |
1 |
5,000～10,000 |
| 186 |
3 |
Clear & clean |
10 |
15 |
15,000~35,000 |
| 1636 |
3 |
Clear & clean |
3 |
5 |
20,000-30,000 |
| 1656 |
3 |
Clear & clean |
5 |
5 |
50,000 |
| 1701 |
2 |
Clear & clean |
6 |
5 |
2,800~5,700 at 65°C |
| 1702 |
2 |
Clear & clean |
6 |
5 |
3,000~11,000 at 60°C |
| 1703 |
2 |
Clear & clean |
6 |
3 |
3,500-4,800 |
Oligomer